BASF Black Ultrafuse PP GF30 Filament 1.75mm, 0.7 kg

The BASF Ultrafuse PP GF 30 is a polypropylene-based composite filament reinforced with 30% glass fiber. The material features high stiffness and allows producing light-weight, dimensionally accurate parts. Excellent resistance to chemicals as well as high heat resistance make it a perfect solution for the use in harsh environments, for example, in automotive industry. Due to UV resistance and low moisture uptake, parts made of the Ultrafuse PP GF30 can be used outdoors and exposed to direct sunlight.

As the Ultrafuse PP GF30 is an abrasive material, a hardened nozzle should be used for printing. The recommended nozzle temperature is 240–260 °C, and PP tape or PPGF adhesive for the print surface are highly advisable.

The BASF Ultrafuse PP GF30 is ideal for many industrial applications requiring high performance in unfavorable environments. It is used in transportation, automotive, oil and gas industries. The material is well suited for production of tools and assembly fixtures as well as for manufacturing of sports equipment to be used outdoors.

Specifications

• Print bed temperature: 20–40 °C 
• Nozzle temperature: 240–260 °C
• Recommended bed surface: PP strapping tape / PPGF adhesive
• Nozzle diameter: ≥ 0.6 mm
• Print speed: 30–80 mm/s
• Printed part density: 1066 kg/m³
• Tensile strength, ISO 527: 41.7 MPa (XY), 15.9 MPa (ZX)
• Elongation at break, ISO 527: 4.4% (XY), 0.8% (ZX)
• Young’s modulus, ISO 527: 2628 MPa (XY), 2242 MPa (ZX)
• Flexural strength, ISO 178: 76.8 MPa (XY), 95.3 MPa (XZ), 19.3 MPa (ZX)
• Flexural modulus, ISO 178: 3507 MPa (XY), 4026 MPa (XZ), 1671 MPa (ZX)
• Flexural strain at break, ISO 178: 4.6% (XY), 3.3% (XZ), 1.3% (ZX)
• Impact strength Charpy (notched), ISO 179-2: 5.3 kJ/m² (XY), 5.2 kJ/m² (XZ), 1.2 kJ/m² (ZX)
• Impact strength Charpy (unnotched), ISO 179-2: 23.1 kJ/m² (XY), 25.8 kJ/m² (XZ), 2.5 kJ/m² (ZX)
• Impact strength Izod (notched), ISO 180: 5.6 kJ/m² (XY), 6.2 kJ/m² (XZ), 1.4 kJ/m² (ZX)
• Impact strength Izod (unnotched), ISO 180: 20.5 kJ/m² (XY), 2.4 kJ/m² (XZ), 2.6 kJ/m² (ZX)
• HDT at 1.8 MPa: 793 °C
• HDT at 0.45 MPa: 127 °C
• Glass transition temperature: -5 °C
• Crystallization temperature: 125 °C
• Melting temperature: 158 °C

Spool specs

• Filament diameter: 1.75 mm
• Spool weight: 0.7 kg
• Available colors: Black
• Color attribute: Solid

The BASF Ultrafuse PP GF 30 1.75 mm 3D printing filament is sold in 0.7 kg spools. It comes vacuum-sealed with desiccant.